Title	Direct energy bandgap group IV alloys and nanostructures
Degree	PhD
Option	Applied Physics
Advisory Committee	Advisor Name Title Harry A. Atwater Committee Chair Kerry J. Vahala Committee Member Micheal Ortiz Committee Member Stephen Quake Committee Member William L. Johnson Committee Member
Keywords	bandstructure engineering growth instabilities phase separation quantum dots self assembly monolithic integration nanostructures nanowire arrays
Date of Defense	2002-01-16
Availability	unrestricted
Abstract Novel group IV nanostructures were fabricated and the optical properties of such nanostructures were investigated for monolithic integration of optically active materials with silicon. The SnxGe1-x alloy system was studied due to the previous demonstration of an indirect to direct energy bandgap transition for strain-relieved SnxGe1-x films on Si(001). In addition, quantum confined structures of Sn were fabricated and the optical properties were investigated. Due to the small electron effective mass of a-Sn, quantum confinement effects are expected at relatively large radii. Coherently strained, epitaxial SnxGe1-x films on Ge(001) substrates were synthesized with film thickness exceeding 100 nm for the first time. The demonstration of dislocation-free SnxGe1-x films is a step toward the fabrication of silicon-based integrated infrared optoelectronic devices. The optical properties of coherently strained SnxGe1-x/Ge(001) alloys were investigated both theoretically and experimentally. Deformation potential theory calculations were performed to predict the effect of coherency strain on the extrema points of the conduction band and the valence band. The energy bandgap of SnxGe1-x/Ge(001) alloys was measured via Fourier transform infrared spectroscopy. Coherency strain did not change the SnxGe1-x energy bandgap when the strain axis was along [001] but deformation potential theory predicted the absence of an indirect to direct energy bandgap transition when the strain axis was along [111]. In addition to being the only group IV alloy exhibiting a direct energy bandgap, when grown beyond a critical thickness, SnxGe1-x/Ge(001) exhibits an interesting phenomenon during MBE growth. Sn segregates via surface diffusion to the crest of a surface undulation during growth and forms ordered Sn-enriched SnxGe1-x rods oriented along [001]. The SnxGe1-x alloy system was used as a model system to gain insight to the physical mechanisms governing self-assembly and ordering during molecular beam epitaxy. Sn nanowires were fabricated in anodic alumina templates with lengths exceeding 1 mm and diameters on the order of 40 nm. Anodic alumina templates can be fabricated non-lithographically with ordered domains of hexagonally packed pores greater than 1 mm and pore densities on the order of 1011 cm-2. The achievement of single crystal Sn nanowires fabricated using pressure injection in porous alumina templates was demonstrated. The fabrication of a-Sn quantum dots embedded in Ge was achieved by annealing 1 mm thick SnxGe1-x films. The measured diameter of the quantum dots was 32 nm and a 10% size variation was observed. Optical transmittance measurements yield a value of 0.45 eV for the direct energy bandgap as a result of quantum confinement. A high degree of tunability of the bandgap energy with the quantum dot radius is expected for a-Sn. Thus quantum-confined structures of a-Sn are promising for optoelectronic device applications.